TU 2246-093-00203387-07
The sheets are designed for manufacturing, mechanical method - vakuumformovaniya, sanitary products appointments: solaria, basins, baths, Jacuzzi, shower trays, booths and related items. He also used in the advertising industry, and as an ornamental and facing material used in different climates.
Temperature operating sheets and articles are from - 40 ° C to +80 ° C. Sheets ABS / PMMA (PMMA - polimetilmetakrilat, acrylic) and articles thereof resistant to wet disinfection.
Specifications
Depending on the applications sheets are made of three types:
- Sheets, with a minimum thickness of the PMMA - 10% of the total thickness, intended for the manufacture of swimming pools, bathtubs, shower trays, sinks.
- Sheets, with a minimum thickness of the PMMA - 5% of the total thickness, intended for the manufacture of shower trays, sinks, walls ablutions, panels for baths.
- Double ABS/PMMA- sheets with a thickness polimetilmetakrilata 20%, used as an ornamental and facing material, and is also used in the advertising industry.
Appearance sheets must be consistent with the control model adopted in due course.
The color plates must conform to the color of granular material or with white sheets dyes in the extrusion - a standard form.
On the front side there should be no bubbles, voids, nadryvov, oil stains and local changes in color. On the face of the sheets are not allowed to include spot foreign emerging to the surface (further point inclusion) and sinks in size from 0.4 to 1.0 mm in the area of 1m2. for all types of leaves of more than 8 pieces. Point and the inclusion of sinks are larger than 1mm are not allowed.
1.5 The sheets should have the dimensions shown in the table.
The nominal size, mm |
Deviation sheets, mm |
The length of 600 to 4000 |
+5 |
Note:
In agreement with the customer is allowed to produce lists of other sizes.
According to the physical and mechanical performance sheets must conform to the standards set forth in the table.
Name of target |
The norm for the types of |
Test Method |
||
I |
II |
III |
||
1.Udarnaya viscosity Sharpi kJ (M2 (KD sm/sm2) in |
Without a bit. |
Without azr. |
Without a bit. |
Clause 5.6 of this TU |
2.Otnositelnoe elongation at break%, at least |
15 |
12 |
8 |
GOST 11262 and p.5.7 of this TU |
3.Usadka %, no more sheets for a nominal thickness: |
|
|
|
Clause 5.8 of this TU |